Вулканизатор предварительно диспергированной резины С-80
Система отверждения серой для резиновых смесей
Полимерно-связанный каучуковый вулканизирующий агент сера маточная смесь
CTMIX С-80 GE F200
Vulcaniz АТОР Сера ( S )
|
ACTIVE
M
A
T
E
R
I
A
L
|
Sulfur
Chemical Formula: S8
M.W.: 256.52
CAS: 7704-34-9
EINECS: 231-722-6
|
PROPERTIES:
Sulfur is a vulcanizing agent for natural and dialkene synthetic rubber while it is difficult for traditional sulfur powders to disperse in rubber homogeneously. It is extremely important for light- colored rubber products to use Actmix®S-80 due to excellent dispersity to avoid brown-spot appearance and minimize the defects of vulcanizates.
DOSAGE:
0.2-4phr, depending on different use and features.
|
APPLICATIONS:
Rubber products exposed to dynamic stress; kinds of soft rubber compounds, sulfur-flawless light-colored rubber compounds.
TYPICAL VALUES:
Melting point: 114℃
Purity: Min 99.5%
Ash content: Max 0.2%
Heating loss content: Max 0.3%
63μm sieve residue: Max 0.5%
|
|
M
A
S
T
E
R
B
A
T
C
H
|
PRODUCT
|
Active
Content (%)
|
Color
|
Filtration
(μm)
|
Binder
|
Sulfur Content
(%)
|
Density (g/cm3)
|
|
Actmix®
S-80GE F200
|
80
|
Yellow Granules
|
200
|
EPDM/EVM
|
79.5
|
1.48
|
|
* Binder type can be customized. Except EPDM/EVM, others binders, such as NBR, SBR, AR, ECO also can be available for.
SAFETY&TOXICITY:
Please refer to related SDS.
PACKAGING&STORAGE:
Net weight 25kg/PE bags lined carton; Net weight 600 or 750 kg/pallet.
Shelf-life : 1 year in its original packaging
Stored in a dry and cool place.
|
По сравнению с традиционными порошками S , Actmix®S-80GE F200 позволяет:
Беспыльные продукты с полной фильтрацией до 63 мкм, отсутствие сенсибилизации кожи, предотвращение ожогов или даже взрыва при смешивании с воздухом.
Эффективная гарантия стабильности и активности серы за счет предварительно диспергированной маточной смеси.
Продукты без липкости при комнатной температуре, удобстве и точности ингредиентов.
Более низкая вязкость по Муни при более низкой температуре (50 ℃), более высокое качество дисперсии, отсутствие появления коричневых пятен.
Без примесей, забитый фильтр без экструзионных продуктов, снижение количества брака и более высокая производительность благодаря фильтрации.
Более широкая совместимость с другими эластомерами.
G: гранулы, P: пластина, E: связующее EPDM, N: связующее NBR, S: связующее SBR, A: связующее ACM, EO: связующее ECO, F200: фильтрация и микронное число фильтра
|
List of Actmix®Pre-dispersed Rubber Chemicals & Additives
|
|
No.
|
Chemical name
|
Active material
|
Active Content(%)
|
|
Actmix® Rubber Accelerators
|
|
1
|
Actmix® CBS-80GE F140
|
N-cyclohexyl-2-benzothiazyl sulfenamide
|
80
|
|
2
|
Actmix® DOTG-75GA F140
|
N,N’-di-o-tolyl guanidine
|
75
|
|
3
|
Actmix® DPG-80GE F140
|
N,N'-diphenyl guanidine
|
80
|
|
4
|
Actmix® DPTT-70GE F140
|
Dipentamethylene thiuram tetrasulfide
|
70
|
|
5
|
Actmix® ETU-80GE F140
|
N,N'-ethylene thiourea
|
80
|
|
6
|
Actmix® MBT-80GE F140
|
2-mercapto-benzthiazol
|
80
|
|
7
|
Actmix® MBTS-75GE F140
|
Dibenzothiazyl disulphide
|
75
|
|
8
|
Actmix® TBBS-80GE F200
|
N-tert.-butyl-2-benzothiazyl sulphenamide
|
80
|
|
9
|
Actmix® TBzTD-70GE F140
|
Tetrabenzylthiuram disulphide
|
70
|
|
10
|
Actmix® TDEC-75GE F140
|
Tellurium diethyl dithiocarbamate
|
75
|
|
11
|
Actmix® TETD-75GE F200
|
Tetraethylthiuram disulphide
|
75
|
|
12
|
Actmix® TMTD-80GE F140
|
Tetramethylthiuram disulphide
|
80
|
|
13
|
Actmix® TMTM-80GE F500
|
Tetramethylthiuram disulphide
|
80
|
|
14
|
Actmix® ZBEC-70GE F140
|
Zinc dibenzyl dithiocarbamate
|
70
|
|
15
|
Actmix® ZDBC-80GE F140
|
Zinc dibutyl dithiocarbamate
|
80
|
|
16
|
Actmix® ZDEC-75GE F140
|
Zinc diethyl dithiocarbamate
|
75
|
|
17
|
Actmix® ZDMC-80GE F140
|
Zinc dimethyl dithiocarbamate
|
80
|
|
18
|
Actmix® ZDTP-50GE F500
|
Zinc dialkyldithiophosphate
|
50
|
|
19
|
Actmix® ZDT-50GE F500
|
Zinc dialkyldithiophosphate
|
50
|
|
20
|
Actmix® ZBOP-50GE F140
|
Zinc dialkyldithiophosphate
|
50
|
|
21
|
Actmix® TP-50GE F140
|
Zinc dialkyldithiophosphate
|
50
|
|
22
|
Actmix® ZBPD-50GE F140
|
Zinc o,o-dibutylDithiophosphate
|
50
|
|
23
|
Actmix® ZAT-70GE
|
Dithiocarbamate phosphate
|
70
|
|
24
|
Actmix® ACT-70GA/XLA-60
|
Comprehensive accelerator
|
70
|
|
25
|
Actmix® DCBS-80GE F140
|
N,N-Dicyclohexyl-2-Benzothiazole Sulfenamide
|
80
|
|
26
|
Actmix® TiO2-80GE F140
|
Titanium dioxide
|
80
|
|
27
|
Actmix® MBS-80GE F200
|
Benzothiazyl-2-sulphene morpholide
|
80
|
|
28
|
Actmix® ZMBT-70GE F120
|
Zinc 2-mercaptobenzothiazole
|
70
|
|
29
|
Actmix® DETU-80GE F500
|
N,N'-Diethylthiocarbarnide
|
80
|
|
30
|
Actmix®TiBTD-80PE
|
Isobutyl thiuram disulfide
|
80
|
|
31
|
Actmix® TBTD-40
|
Tetrabutyl Thiuram Disulfide
|
40
|
|
32
|
Actmix® TBTD-55PE
|
Tetrabutyl Thiuram Disulfide
|
55
|
|
33
|
Actmix®MTT-80GE F500
|
3-methyl-2-Thiazolidinethione
|
80
|
|
Synergistic Combination Accelerator
|
|
1
|
Actmix® EG3M-75GE F140
|
Comprehensive accelerator
|
75
|
|
2
|
Actmix® EG3T-75GE F140
|
Comprehensive accelerator
|
75
|
|
3
|
Actmix® EG3A-75GE F140
|
Comprehensive accelerator
|
75
|
|
4
|
Actmix® LHG-80GE F140
|
Comprehensive accelerator
|
80
|
|
Rubber Vulcanization/Curing/Cross-linking Agent
|
|
1.
|
Actmix® S-80GE F200
|
Sulphur
|
80
|
|
2.
|
Actmix® IS60-75GE F500
|
insoluble sulphur
|
75
|
|
3.
|
Actmix® IS90-65GE F500
|
insoluble sulphur
|
65
|
|
4.
|
Actmix® DTDM-80GE F200
|
Dithiodimorpholine
|
80
|
|
5.
|
Actmix® PDM-75GE F140
|
N,N’-m-phenylenebismaleimide
|
75
|
|
6.
|
Actmix® TCY-70GEO F140
|
2,4,6-Trimercapto-s-triazine
|
70
|
|
7.
|
Actmix® TCY-70GA
|
2,4,6-Trimercapto-s-triazine
|
70
|
|
8.
|
Actmix® HMDC-70GA
|
Hexamethylene diamine carbamate
|
70
|
|
9.
|
Actmix® CLD-80GE F500
|
Caprolactmadisulfide
|
80
|
|
10.
|
Actmix® BCS-41/IIR
|
Alkyl phenolic resin combined with ZnO
|
41
|
|
11.
|
Actmix® TAC-50
|
Trially cyanurate
|
50
|
|
Rubber Vulcanization Activator
|
|
1
|
Actmix® ZnO-80GE F140
|
Zinc oxide
|
80
|
|
2
|
Actmix® ZnO-85C
|
Active Zinc oxide
|
85
|
|
3
|
Actmix® MgO-75GE F140
|
Magnesium oxide
|
75
|
|
4
|
Actmix®PbO-80GE
|
Lead oxide
|
80
|
|
5
|
Actmix®Pb3O4-80GE
|
Lead tetroxide
|
80
|
|
6
|
Actmix®KST-50GA
|
Potassium stearate, Cross-linking activator for ACM
|
50
|
|
7
|
Actmix®NAST-50GA
|
Sodium stearate, Cross-linking activator for ACM
|
50
|
|
Rubber Foaming Agent
|
|
1
|
Actmix® ADC-75GE
|
Azodicarbonamide
|
75
|
|
2
|
Actmix® ADC-50GE
|
Azodicarbonamide
|
50
|
|
3
|
Actmix® ADC/EVA
|
Azodicarbonamide, complex active substance in EVA
|
|
|
4
|
Actmix® OBSH-75PE
|
Oxybis(benzenesulfonyl hydrazide)
|
75
|
|
5
|
Actmix® OBSH-50GE
|
Oxybis(benzenesulfonyl hydrazide)
|
50
|
|
6
|
Actmix® DPT/PE; DPT/PC
|
N, N-dinitroso pentamethylene tetramine
|
|
|
7
|
Actmix®HDU/GE
|
Microspheres foaming agent
|
50-70
|
|
8
|
Actmix®LDU/GE
|
Microspheres foaming agent
|
50-70
|
|
9
|
Actmix®EM304-40PE
|
Microspheres foaming agent
|
40
|
|
10
|
Actmix®ZBS-80GE
|
Foaming agent activator
|
80
|
|
Rubber Scorching Retarder
|
|
1
|
Actmix® Retarder E-80GE
|
N-Phenyl-N-(Trichloromethylsulfenyl)-Benzene Sulfonamide
|
80
|
|
2
|
Actmix® CTP-80GE F500
|
N-(Cyclohexylthio)-phthalimide
|
80
|
|
Rubber Antioxidant
|
|
1
|
Actmix® MBI-80GE F140
|
2-Mercaptobenzimidazole
|
80
|
|
2
|
Actmix® MMBI-70GE F200
|
Methyl-2-mercaptobenzimidazole
|
70
|
|
3
|
Actmix®NDBC-75GEO
|
Nickel dibutyl dithiocarbamate
|
75
|
|
4
|
Actmix®NDBC-75GE
|
Nickel dibutyl dithiocarbamate
|
75
|
|
5
|
Actmix®ZMMBI-70GE F200
|
Zinc methyl-2-mercaptobenzimidazole
|
70
|
|
6
|
Actmix®ZMMBI-50GE F200
|
Zinc methyl-2-mercaptobenzimidazole
|
50
|
|
Rubber Adhesive Agent
|
|
1
|
Actmix®Resorcinol-80GS
|
Resorcinol
|
80
|
|
2
|
Actmix®HEXA-80GE F500
|
Hexamethylene tetramine
|
80
|
|
3
|
Actmix® HMMM-50GE F140
|
Hexamethoxy methyl melamine resin
|
50
|
|
4
|
Actmix® Si69-50GE F200
|
Bis[3-(triethoxysilyl)propyl] tetrasulfide
|
50
|
|
Rubber Hygroscopic Agent/Defoaming/Desiccant Agent
|
|
1
|
Actmix®CaO-80GE F200
|
Calcium oxide
|
80
|
|
Rubber Biocide-algaecide Agent
|
|
1
|
Actmix®BCM-80GE F140
|
Carbendazim
|
80
|
|
Rubber deodorant
|
|
1
|
Actmix®LHRD/GE
|
Inorganic silicate
|
75
|
Мы - компания Ningbo Actmix Rubber Chemicals Co., Ltd , ведущий производитель химикатов и добавок для полимерной резины, специально используемых для автомобильной промышленности, с высоким качеством и конкурентоспособной ценой.
В число наших конечных заказчиков входят многие производители автомобильных резиновых уплотнений, шин по всему миру.
* Заводы Hutchinson во Франции / Испании / Бразилии
* Заводы Cooper Standard Auto Parts Китай / Бразилия / Корея / Европа;
* Nishikawa Seal System (заводы в Китае / Индии / Японии);
* Kinugawa Rubber Industry (заводы в Китае / Японии);
* Заводы Hexpol Europe / China
Химикаты для каучука Actmix® могут применяться для:
1. Автомобильная резиновая уплотнительная лента.
2. Технические резиновые детали, щетки стеклоочистителя, уплотнение, шланг, ремень, антивибрационные и т. Д.
3. Резиновые шины
4. Резиновая подошва обуви, сапоги и т. Д.
Actmix® Ассортимент предварительно диспергированных маточных смесей резиновых химикатов:
1. Ускорители тиазола, тиурама, дитиокарбамата, гуандина и тиомочевины
2. Вулканизирующий агент, активатор вулканизации.
3. Антиоксидант
4. Замедлители горения
5. Пенообразователь.
6. Экологичный ускоритель: ZDTP-50, Retarder E-80, ZBEC-70, TBzTD-70 и т. Д.
Теперь у нас есть дистрибьюторы в более чем 15 странах, таких как Германия, Россия, Польша, Япония, Корея, Бразилия, Таиланд и т. Д. Мы можем настраивать продукцию в соответствии с потребностями клиентов.
При необходимости мы можем предоставить небольшое количество образцов для лабораторных испытаний в любое время.
Добро пожаловать, чтобы отправить нам запрос!
Нинбо Actmix Rubber Chemicals Co., Ltd.
Сайт: http://www.actmix.cn/
Contact Now